Edge Stresses in Alumina/Zirconia Laminates

Using the technique of fluorescence piezospectroscopy, we determine the distribution of thermal residual stresses across the edges of three laminated alumina/zirconia composites. We develop a methodology for separating the measured stress state into microstresses that result from grain-to-grain thermal mismatch and macrostresses that result from lamination-induced thermal mismatch between individual plies. Comparison between the measured edge-stress distributions and those calculated based on a simple force superposition model shows good agreement, indicating that the laminate system is well approximated as linear elastic. Given the experimental confirmation of significant edge stresses in multi-ply laminates, the possibility of failure initiating at composite edges must be considered in the the design of surface-compressed laminate structures with the aim of mediating the detrimental effect of surface flaws.