Hybrid inorganic-organic proton conducting membranes based on Nafion and 5 wt% of MxOy (M = Ti, Zr, Hf, Ta and W). Part II: Relaxation phenomena and conductivity mechanism.

In this report, we are presenting studies of the effect of MxOy nanopowders on the thermal, mechanical and electrical properties of [Nafion/(MxOy)n] membranes with M= Ti, Zr, Hf, Ta and W and n = 5 wt%. Five homogeneous membranes with thicknesses ranging from 170 to 350m were studied. The thermal transitions characterizing [Nafion/(MxOy)n] materials were investigated by modulated differential scanning calorimetry (MDSC). The mechanical parameters and relaxation processeswere studied on temperature by dynamical mechanical analyses (DMA). Broadband dielectric spectroscopy (BDS) was used to study the conductivity mechanism and dielectric relaxation events in bulk materials. DMA investigations showed two distinct relaxation events. The first relaxation phenomenon, detected at about 19 oC, was attributed to the mechanical -relaxation mode of Nafion. The second event, revealed in the temperature range 100-135 oC, was assigned to the mechanical -relaxation mode of Nafion. The electric response of membranes was studied by BDS measurements in the frequency and temperature range respectively of 40 Hz-10MHz and 5-135 oC. Real and imaginary components of permittivity (?*(?) = ? (?)-i?(?)) and conductivity spectra (*(?) = (?) + i(?))were analyzed. Conductivity spectra allowed us to accurately determine the dc of membranes at 100% RH as a function of T. Two relaxation peakswere detected in the ?*(?) profiles. The lowfrequency relaxation eventwas attributed to the-relaxationmodeof fluorocarbon chains of Nafion. The high frequency relaxation peak corresponds to the -relaxation of acid side groups. The results allowed us to conclude that MxOy influences: (a) the relaxations of both the hydrophobic and the hydrophilic domains of Nafion polymer host; (b) the thermal stability range of conductivity (SRC) and the dc of membranes. In conclusion, nanofillers affect the macromolecular dynamics of Nafion-based polymer host owing to the formation of dynamic cross-links, R-SO3H· · ·MxOy· · ·HSO3-R, in hydrophilic polar cages. The membranes doped with HfO2 andWO3 oxoclusters present a stability range of conductivity of 5 oC<=T<=135 oC and give rise to dc values of respectively 2.8×10-2 and 2.5×10-2 Scm-1 at 135 oC and 100% RH. These latter conductivity values make the nanocomposite membranes based on HfO2 andWO3 oxoclusters very promising materials for the application in polymer electrolyte fuel cells (PEMFCs) and direct methanol fuel cells (DMFCs).