3D printing of fine alumina powders by binder jetting

Additive manufacturing of ceramics is still at an early-development stage; however, the huge interest in custom production of these materials has led to the development of different techniques that could provide highly performing devices. In this work, alumina (alpha-Al2O3) components were produced by binder jetting 3D printing (BJ), a powder-based technique that enables the ex-situ thermal treatment of the printed parts. The employment of fine particles has led to high green relative density values (>60 %), as predicted by Lubachevsky-Stillinger algorithm and DEM modelling. Then, extended sintering has been observed on samples treated at 1750 degrees C that have reached a final density of 75.4 %. Finally, the mechanical properties of the sintered material have been assessed through bending test for flexural resistance and micro-indentation for Vickers hardness evaluation.