Low-temperature atomic layer deposition of MgO thin films on Si

Magnesium oxide (MgO) films have been grown by atomic layer deposition in the wide deposition temperature window of 80-350 °C by using bis(cyclopentadienyl)magnesium and HO precursors. MgO thin films are deposited on both HF-last Si(1 0 0) and SiO/Si substrates at a constant growth rate of ~0.12 nm cycle. The structural, morphological and chemical properties of the synthesized MgO thin films are investigated by x-ray reflectivity, grazing incidence x-ray diffraction, time-of-flight secondary ion mass spectrometry and atomic force microscopy measurements. MgO layers are characterized by sharp interface with the substrate and limited surface roughness, besides good chemical uniformity and polycrystalline structure for thickness above 7 nm. C-V measurements performed on Al/MgO/Si MOS capacitors, with MgO in the 4.6-11 nm thickness range, allow determining a dielectric constant (?) ~ 11. Co layers are grown by chemical vapour deposition in direct contact with MgO without vacuum-break (base pressure 10-10 Pa). The as-grown Co/MgO stacks show sharp interfaces and no elements interdiffusion among layers. C-V and I-V measurements have been conducted on Co/MgO/Si MOS capacitors. The dielectric properties of MgO are not influenced by the further process of Co deposition. © 2013 IOP Publishing Ltd.