A study of extended defects in surface damaged crystals

We have analyzed by transmission electron microscopy silicon and GaAs crystals polished with sandpapers of different grain size. The surface damage induced a crystal permanent convex curvature with a radius of the order of a few meters. The curvature is due to a compressive strain generated in the damaged zone of the sample. Contrary to what was reported in the literature, the only defects detected by transmission electron microscopy were dislocations penetrating a few microns from the surface. Assuming the surface damage as a kind of continuous indentation, a simple model able to explain the observed compressive strain is given.