Fluorine redistribution and incorporation during solid phase epitaxy of preamorphized Si

The redistribution of fluorine during solid phase epitaxial regrowth (SPER) of preamorphized Si has been experimentally investigated, explained, and simulated, for different F concentrations and temperatures. We demonstrate, by a detailed analysis and modeling of F secondary ion mass spectrometry chemical-concentration profiles, that F segregates in amorphous Si during SPER by splitting in three possible states: (i) a diffusive one that migrates in amorphous Si; (ii) an interface segregated state evidenced by the presence of a F accumulation peak at the amorphous-crystal interface; (iii) a clustered F state. The interplay among these states and their roles in the F incorporation into crystalline Si are fully described. It is shown that diffusive F migrates by a trap limited diffusion mechanism and also interacts with the advancing interface by a sticking-release dynamics that regulates the amount of F segregated at the interface. We demonstrate that this last quantity determines the regrowth rate through an exponential law. On the other hand we show that neither the diffusive F nor the one segregated at the interface can directly incorporate into the crystal but F has to cluster in the amorphous phase before being incorporated in the crystal, in agreement with recent experimental observations. The trends of the model parameters as a function of the temperature are shown and discussed obtaining a clear energetic scheme of the F redistribution and incorporation in preamorphized Si. The above physical understanding and the model could have a strong impact on the use of F as a tool for optimizing the doping profiles in the fabrication of ultrashallow junctions.