Optical properties of BaY2F8:Ce3+

The optical properties of Ce3+-doped BaY2F8 crystals were investigated under selective laser excitation and x-ray irradiation. In both cases, the emission spectrum is dominated by the characteristic doublet transition from the lowest energy level of the 5d configuration to the spin-orbit split 2F ground state of Ce3+. Excitation bands at 4.1, 5.0, 5.9 and 6.2 eV, due to transitions between 4f and split 5d levels were observed. The emission time decay was satisfactorily analyzed by a single exponential component, char-acterized by a decay time of approximately 28 ns at 10 K and slightly increasing with temperature. A monotonic temperature quenching of the photo-luminescence intensity was observed; on the other hand, the temperature dependence of radio-luminescence intensity is modulated by the presence of shallow traps competing with Ce3+ ions in carrier trapping during irradiation.