Fiber yield and quality of fiber nettle (Urtica dioica L.) cultivated in Italy

To evaluate the production potential of fiber nettle crops in Tuscany (Italy), a German clone of fiber nettle was cultivated during 2006-2007. Although a longer experimentation is essential, the two first years of trials showed that the German clone used also seems to give good results in term of growth and fiber yield in an environment like central Italy, with higher temperatures and generally lower rainfall. Indeed the stalk mean dry matter obtainedwas about 15.4Mgha-1 with a mean fiber content of about 11% of stalk dry matter, and the resulting fiber yield was 1696 kg ha-1, comparable to or higher than those reported in the literature. The differences in chemical, physical and mechanical characteristics of fibers extracted from different portions of stalks seemed to indicate an intrinsic heterogeneity of the fibers along the stem. Fiber mean diameter values ranged from 47 to 19µm and fiber length from 43 to 58 mm moving from stalk bottom to top. Tensile strength of the bottom part of the stalk was much lower than that of the other parts, with mean values of about 24 and 60 cN tex-1, respectively. More constant mean values along the stalk were found for the elongation parameter (2.3-2.6%). Lignin content decreased moving toward the stalk top from about 4.4% to 3.5%. These physical-mechanical characteristics confirmed the potential of the fibers of nettle cultivated in Tuscany to be used for textile purposes. Indeed theywere similar to hemp fibers in diameter, lignin content and elongation, and similar to flax or cotton in tensile strength.