Blends of syndiotactic polystyrene with SEBS triblock copolymers

Blending of styrene-b-(ethylene-co-1-butene)-b-styrene (SEBS) triblock copolymers with syndiotactic polystyrene (PSsyn) has been performed in a Brabender mixer above the higher glass transition temperature of the triblock copolymer but below the PSsyn melting point. The large excess of the triblock copolymer over the homopolymer as well as the significant amount of plasticized amorphous PSsyn phase allowed the easy processing under the used temperature conditions with good interface compatibility. The consequent interfacial adhesion between the amorphous PS phase and the unmelted PSsyn crystallites affects both the final morphology of the blend as well as its dynamic behaviour. Indeed, such solid particles act as reinforcing point of the overall blend structure, as evidenced by Scanning Electron Microscopy (SEM). Moreover, they contribute to a Tg increase of the blends and to an appreciable conservation of mechanical properties at temperatures higher than the Tg of the PS blocks of SEBS.