Structural modifications and electrical properties in ion-irradiated polymide

The ion beam-induced modification of the electrical conductivity and the related structural features have been studied for thin films of poly-iso-quinazolindione (PIQ). The films, deposited onto specially designed test patterns, were irradiated by using 600 keV Ar+ ions in the fluence range between 1x10(14) to 1x10(15) ions/cm(2). The beam-induced chemical and structural modifications have been investigated by using X-ray Photoelectron Spectroscopy (XPS) and Raman Spectroscopy, while the modification of the electrical properties was followed by performing a complete set of I/V measurements. In particular, we obtained the evidence of the occurrence of a true semiconducting state for samples irradiated at fluence around 6x10(14) ions/cm(2), which exhibited the characteristic I/V features of a Schottky diode. Samples irradiated at higher fluence showed a good conductivity, with a saturation value of 4 x 10(2) Omega cm. The XPS data demonstrate that the modification of the electrical properties is due to the progressive formation with increasing ion fluence of a dense amorphous carbon network, while Raman data suggest the existence of different structural features, respectively for the semiconducting and the conducting phases. (C) 1999 Elsevier Science B.V. All rights reserved.