Polyimide hollow fiber membranes for CO2 separation from wet gas mixtures

Matrimid®5218 hollow fiber membranes were prepared using the dry-wet spinning process. The transport properties were measured with pure gases (H2, CO2, N2, CH4 and O2) and with a mixture (30% CO2 and 70% N2) in dry and wet conditions at 25 °C, 50 °C, 60 °C and 75 °C and up to 600 kPa. Interesting values of single gas selectivity up to 60 °C (between 31 and 28 for CO2/N2 and between 33 and 30 for CO2/CH4) in dry condition were obtained. The separation factor measured for the mixture was 20% lower compared to the single gas selectivity, in the whole temperature range analyzed. In saturation conditions the data showed that water influences the performance of the membranes, inducing a reduction of the permeance of all gases. Moreover, the presence of water caused a decrease of single gas selectivity and separation factor, although not so significant, highlighting the very high water resistance of hollow fiber membrane modules.