Reactivity and magnetism of Fe/inas(100) interfaces

Interface reaction and magnetism of epitaxially-grown Fe on InAs(100) are studied by core-level photoemission (As 3d and In 4d) and Fe 2p X-ray magnetic circular dichroism using synchrotron radiation. The reactivity of Fe/InAs(100) is relatively low compared to that of other interfaces involving deposition of 3d metals on III-V semiconductors. As a consequence, we observe a magnetic signal at Fe L2, 3 edges for the lowest thicknesses studied (1 ML). The atomic magnetic moment reaches a value close to that of the bulk ?-Fe (2.2 ? B) for Fe coverages exceeding 5 ML. A ferromagnetic compound with approximate stoichiometry of FeAs is formed at the interface. The orbital magnetism represents between 12 and 20% of the total momentum, due to 3d density of states depletion and to crystal-field modification of the electronic levels. These properties make the Fe/InAs(100) interface very promising for spin-tunneling devices.